Fiberglass composite XEGLASS 22 series

thermosetting resinfor the aerospace industrydensity

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 15000 Tensile Strength at break 5 mm/min ISO 527 MPa 220 Tensile Elongation at break 5 mm/min ISO 527 % 3,2 Flexural Modulus 2 mm/min ISO 178 MPa 13000 Flexural Strength 2 mm/min ISO 178 MPa Flexural Stress at 3,5% strain 2 mm/min ISO 178 MPa 335 Flexural Strain at break 2 mm/min ISO 178 % Deflection at break mm Deflection at 3,5% strain mm Notched Izod Impact Strength 23 °C ; 50 % RH ISO 180 kJ/m2 18 Unnotched Izod Impact Strength 23 °C ; 50 % RH ISO 180 kJ/m2 90 Notched Izod Impact Strength -30 °C ISO 180 kJ/m2 16 Unnotched Izod Impact Strength -30 °C ISO 180 kJ/m2 67