Fiberglass composite XEBRID 29 series

carbon fiberthermoplastic resinfor the aerospace industry

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 30000 Tensile Strength at break 5 mm/min ISO 527 MPa 265 Tensile Elongation at break 5 mm/min ISO 527 % 1,8 Flexural Modulus 2 mm/min ISO 178 MPa 25000 Flexural Strength 2 mm/min ISO 178 MPa 390 Flexural Stress at 3,5% strain 2 mm/min ISO 178 MPa Flexural Strain at break 2 mm/min ISO 178 % 2,2 Deflection at break mm Deflection at 3,5% strain mm Notched Izod Impact Strength 23 °C ; 50 % RH ISO 180 kJ/m2 6 Unnotched Izod Impact Strength 23 °C ; 50 % RH ISO 180 kJ/m2 57 Notched Izod Impact Strength -30 °C ISO 180 kJ/m2 4 Unnotched Izod Impact Strength -30 °C ISO 180 kJ/m2 53