Wires titanium

Mechanical resistance: 345 MPa
Elasticity: 275 MPa
Typical elongation: 20 %

... III, IV (ATI 30, 40, 55, 70) • ASTM B 348 - Bars and Billets • AMS 4921 - Bars, Wire, and Forgings • ASTM F 67 - Unalloyed Titanium • ISO 5832-2 - Unalloyed Titanium PHYSICAL PROPERTIES Melting ...

Mechanical resistance: 450 MPa
Elasticity: 380 MPa
Typical elongation: 18 %

... III, IV (ATI 30, 40, 55, 70) • ASTM B 348 - Bars and Billets • AMS 4921 - Bars, Wire, and Forgings • ASTM F 67 - Unalloyed Titanium • ISO 5832-2 - Unalloyed Titanium PHYSICAL PROPERTIES Melting ...

Mechanical resistance: 828 MPa
Elasticity: 759 MPa
Typical elongation: 10 %

... and some important aerospace components. This titanium grade is produced by vacuum arc primary melting followed by a second vacuum arc remelting operation. SPECIFICATIONS • AMS 4930 - Bar, Wire, ...

Diameter: 0.063, 0.093, 0.118, 0.156 in

Please find Titanium Industries available Grade 2 Titanium weld wire illustrated below. Perfect for resilient industrial applications, Grade 2 Titanium weld wire ...

Representative grades TA1, TA2, TA3, TA6, TC4, TC5, TC10 Supply method: sheet, rod, plate, wire Please contact us for custom other non-label numbers Representative grades TA1, TA2, TA3, TA6, TC4, TC5, TC10

Diameter: 0.8 mm - 18 mm

ISO 24034 GOST 27265 Hermith 64 for Additive Manufacturing

Mechanical resistance: 827 MPa - 931 MPa
Typical elongation: 10, 8 %
Diameter: 50.8 mm - 152.4 mm

Ti-6Al-4V is a kind of typical α＋β titanium alloy, which is of medium/high strength, excellent fracture toughness, fatigue performance and good processing performance. Ti-6Al-4V alloy has most widely application scope ...

Mechanical resistance: 827 MPa - 931 MPa
Elasticity: 862,000, 827,000 Pa
Typical elongation: 10, 8 %

Ti-6Al-4V is a kind of typical α＋β titanium alloy, which is of medium/high strength, excellent fracture toughness, fatigue performance and good processing performance. Ti-6Al-4V alloy has most widely application scope ...

Mechanical resistance: 827 MPa - 931 MPa
Typical elongation: 8, 10 %
Diameter: 50.8 mm - 152.4 mm

Ti-6Al-4V is a kind of typical α＋β titanium alloy, which is of medium/high strength, excellent fracture toughness, fatigue performance and good processing performance. Ti-6Al-4V alloy has most widely application scope ...

Mechanical resistance: 483 MPa - 620 MPa
Typical elongation: 15 %
Diameter: 2 mm - 6 mm

Ti-3Al-2.5V is a kind of near α titanium alloy, whose tensile strength at the room temperature and high temperature are higher by 20% to 50% than that of CP titanium, and welding and cold forming performance ...

Mechanical resistance: 827 MPa - 931 MPa
Typical elongation: 8, 10 %
Diameter: 50.8 mm - 152.4 mm

Ti-6Al-4V is a kind of typical α＋β titanium alloy, which is of medium/high strength, excellent fracture toughness, fatigue performance and good processing performance. Ti-6Al-4V alloy has most widely application scope ...

Mechanical resistance: 827 MPa - 931 MPa
Typical elongation: 8, 10 %
Diameter: 50.8 mm - 152.4 mm

Ti-6Al-4V is a kind of typical α＋β titanium alloy, which is of medium/high strength, excellent fracture toughness, fatigue performance and good processing performance. Ti-6Al-4V alloy has most widely application scope ...

Mechanical resistance: 414 MPa - 448 MPa
Typical elongation: 10 %
Diameter: 2.4 mm - 6.2 mm

... military aircraft in USA and Europe, successfully replacing pure titanium rivets and widely used in riveting of composite material. At present, WST can supply Ti45Nb straight or coiling wires in size ...