Thermoplastic resin composites

Toray Cetex® TC1000 Design is a cost-effective, high-end thermoplastic composite, utilizing the amorphous PEI polymer for outstanding toughness and an inherently outstanding fire, smoke, and toxicity ...

Toray Cetex® TC1100 is a high-end but cost-effective thermoplastic composite material, utilizing a semi-crystalline PPS polymer for excellent mechanical properties and an outstanding chemical and solvent ...

Toray Cetex® TC1200 is a high-end thermoplastic composite material, utilizing the semi-crystalline thermoplastic polymer PEEK for excellent mechanical performance. The long-standing ...

Thickness: 0.24, 0.12 mm

... Cetex® TC1225 is a high-end thermoplastic composite material, utilizing a semi-crystalline engineered low-melt PAEK resin for excellent mechanical performance. The distinctive value of ...

Thickness: 0.16, 0.24, 0.31 mm

Toray Cetex® TC925 FST is a value oriented engineered thermoplastic composite, utilizing polycarbonate (PC) resin for good surface qualities, impact toughness and good fire resistance. Toray ...

... toolbox, we offer a complementary portfolio of composite solutions that facilitate processes and improve the performance of the final component. Advantages of using thermoplastic composite ...

Thermoplastic composites reinforced Carbon Fiber XECARB® 1-C10 10% carbon fiber reinforced PA66 XECARB® 1-C20 20% carbon fiber reinforced PA66 XECARB® 1-C30 30% carbon fiber-reinforced PA66 XECARB® ...

Thermoplastic composites reinforced Carbon Fiber XECARB® 2-C20-ST 20% carbon fiber reinforced PA6 XECARB® 2-C25-ST 25% carbon fiber reinforced PA6 XECARB® 2-C25-STSI-HM1 25% high modulus carbon fiber ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 9000 Tensile Strength at break 5 mm/min ISO 527 MPa 120 Tensile Elongation at break 5 mm/min ISO 527 % 1,9 Flexural Modulus 2 mm/min ISO 178 MPa 7000 Flexural Strength 2 mm/min ...

XECARB® 6-C30-D11 30% carbon fiber-reinforced ether-based TPU

reinforced ester TPU XECARB® 7 XECARB® 7-C30-D14 30% carbon fiber reinforced TPU ester XECARB® 7-C30-D16-A 30% carbon fiber reinforced TPU ester

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 14000 Tensile Strength at break 5 mm/min ISO 527 MPa 200 Tensile Elongation at break 5 mm/min ISO 527 % 3,1 Flexural Modulus 2 mm/min ISO 178 MPa 10500 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 21000 Tensile Strength at break 5 mm/min ISO 527 MPa 205 Tensile Elongation at break 5 mm/min ISO 527 % 1,2 Flexural Modulus 2 mm/min ISO 178 MPa 15000 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 9500 Tensile Strength at break 5 mm/min ISO 527 MPa 120 Tensile Elongation at break 5 mm/min ISO 527 % 5,2 Flexural Modulus 2 mm/min ISO 178 MPa 8500 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 11500 Tensile Strength at break 5 mm/min ISO 527 MPa 150 Tensile Elongation at break 5 mm/min ISO 527 % 3,9 Flexural Modulus 2 mm/min ISO 178 MPa 8500 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 6500 Tensile Strength at break 5 mm/min ISO 527 MPa 100 Tensile Elongation at break 5 mm/min ISO 527 % 5,3 Flexural Modulus 2 mm/min ISO 178 MPa 4500 Flexural Strength 2 mm/min ...