Fiberglass composites

Toray Cetex® TC1100 is a high-end but cost-effective thermoplastic composite material, utilizing a semi-crystalline PPS polymer for excellent mechanical properties and an outstanding chemical and solvent resistance. With ...

Toray Cetex® TC1200 is a high-end thermoplastic composite material, utilizing the semi-crystalline thermoplastic polymer PEEK for excellent mechanical performance. The long-standing use of PEEK in demanding applications ...

Thickness: 0.24, 0.12 mm

... TC1225 is a high-end thermoplastic composite material, utilizing a semi-crystalline engineered low-melt PAEK resin for excellent mechanical performance. The distinctive value of Toray Cetex® TC1225 over other composites ...

... from a single source. From the development idea to SOP all the way to the first components for serial production. In composite development and parts manufacture, we are your technologically competent and solution-oriented ...

Altuglas® acrylic sheet Product range Altuglas® sheet, balanced between performance and aestheticism, can be used as: signs, street furniture, showers, windows (construction and transportation). Combining beauty and transparency, lightness ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 12000 Tensile Strength at break 5 mm/min ISO 527 MPa 180 Tensile Elongation at break 5 mm/min ISO 527 % 2,2 Flexural Modulus 2 mm/min ISO 178 MPa 9500 Flexural Strength 2 mm/min ...

Physical Properties Test Condition Standard Unit Dam / Cond. Density ISO 1183 g/cm3 1,13 Water absorption (Equilibrium value) 23 °C ; 50 % RH % Water absorption (Saturation value) 23°C ; water % Post-shrinkage Parallel ISO 294-4 % Normal ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 30000 Tensile Strength at break 5 mm/min ISO 527 MPa 265 Tensile Elongation at break 5 mm/min ISO 527 % 1,8 Flexural Modulus 2 mm/min ISO 178 MPa 25000 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 14500 Tensile Strength at break 5 mm/min ISO 527 MPa 150 Tensile Elongation at break 5 mm/min ISO 527 % 2,5 Flexural Modulus 2 mm/min ISO 178 MPa 11500 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 7500 Tensile Strength at break 5 mm/min ISO 527 MPa 110 Tensile Elongation at break 5 mm/min ISO 527 % 6,5 Flexural Modulus 2 mm/min ISO 178 MPa 7000 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 12000 Tensile Strength at break 5 mm/min ISO 527 MPa 175 Tensile Elongation at break 5 mm/min ISO 527 % 4,4 Flexural Modulus 2 mm/min ISO 178 MPa 10500 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 10500 Tensile Strength at break 5 mm/min ISO 527 MPa 145 Tensile Elongation at break 5 mm/min ISO 527 % 4,2 Flexural Modulus 2 mm/min ISO 178 MPa 9000 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 15000 Tensile Strength at break 5 mm/min ISO 527 MPa 220 Tensile Elongation at break 5 mm/min ISO 527 % 3,2 Flexural Modulus 2 mm/min ISO 178 MPa 13000 Flexural Strength 2 mm/min ...

Mechanical Properties Tensile Modulus 1 mm/min ISO 527 MPa 16000 Tensile Strength at break 5 mm/min ISO 527 MPa 235 Tensile Elongation at break 5 mm/min ISO 527 % 2,8 Flexural Modulus 2 mm/min ISO 178 MPa 14000 Flexural Strength 2 mm/min ...